A dielectric ceramic is composed of ABO.sub.3 as the main component and a
rare earth element, wherein A represents barium which may be partly
replaced with at least one of calcium and strontium, and B represents
titanium which may be partly replaced with at least one selected from
zirconium and hafnium. At least 70% of crystal grains of the dielectric
ceramic have a cross-section in which a first region containing dissolved
rare earth element occupies 5 to 70% of the area of the cross section and
a second region free of the dissolved rare earth element occupies 10 to
80% of the periphery of the cross-section. A monolithic ceramic capacitor
having thin dielectric ceramic layers composed of this dielectric ceramic
exhibits superior capacitance-temperature characteristics and high
reliability.
Διηλεκτρικός ένας κεραμικός αποτελείται από ABO.sub.3 στοιχείο ως κύριο συστατικό και ένα σπάνιας γης, όπου το Α αντιπροσωπεύει το βάριο που μπορεί να αντικατασταθεί εν μέρει με τουλάχιστον ένα από το ασβέστιο και το στρόντιο, και β αντιπροσωπεύει το τιτάνιο που μπορεί να αντικατασταθεί εν μέρει με τουλάχιστον το ένα που επιλέγεται από το ζιρκόνιο και hafnium. Τουλάχιστον 70% των σιταριών κρυστάλλου στοιχείο στοιχείο διηλεκτρικού του κεραμικού έχουν μια διατομή στην οποία μια πρώτη περιοχή που περιλαμβάνει το διαλυμένο σπάνιας γης καταλαμβάνει 5 70% του τομέα του διαγώνιου τμήματος και μια δεύτερη περιοχή χωρίς διαλυμένο σπάνιας γης καταλαμβάνει 10 80% της περιφέρειας της διατομής. Ένας μονολιθικός κεραμικός πυκνωτής που έχει τα λεπτά διηλεκτρικά κεραμικά στρώματα αποτελεσμένων από χαρακτηριστικά αυτής της τα διηλεκτρικά κεραμικά ικανότητα-θερμοκρασίας εκθεμάτων ανώτερα και την υψηλή αξιοπιστία.