Copolymer DMC-catalyzed polyoxypropylene polyols which exhibit processing latitude similar to base-catalyzed copolymer analogs and homopolyoxypropylene analogs may be prepared by oxyalkylation with a mixture of propylene oxide and ethylene oxide such that a finite ethylene oxide content is maintained in the oxyalkylation reactor for the most substantial part of the oxyalkylation, the polyoxypropylene polyol having randomly distributed oxyethylene moieties which constitute 1.5 weight percent or more of the polyol product. Block copolymer polyols having external blocks containing lesser oxyethylene content than internal blocks and bicompositional compositions containing discrete multimodal and dissimilar and optionally multimodal polyols produced by a continuous addition of starter process are useful as polyols exhibiting greater processing latitude.

El copolímero DMC-catalizo' los polyols del polyoxypropylene que exhiben el proceso de la latitud similar a los análogos base-catalizados del copolímero y los análogos del homopolyoxypropylene se puede preparar por el oxyalkylation con una mezcla del óxido del propylene y del óxido del etileno tales que un contenido finito del óxido del etileno está mantenido en el reactor del oxyalkylation para la parte más substancial del oxyalkylation, el polyol del polyoxypropylene que distribuye aleatoriamente los moieties del oxyethylene que constituyen por ciento de 1.5 pesos o más del producto del polyol. Los polyols del copolímero del bloque que tienen bloques externos el contener de poco contenido del oxyethylene que bloques internos y las composiciones del bicompositional que contienen multimodal y disímil discretos y los polyols multimodal producidos por una adición continua del proceso del arrancador son opcionalmente útiles como polyols que exhiben mayor latitud de proceso.