A low molecular weight, tertiary amide terminated polyamide may be blended with a liquid hydrocarbon to form a transparent composition having gel consistency. The tertiary amide terminated polyamide may be prepared by reacting "x" equivalents of dicarboxylic acid wherein at least 50% of those equivalents are from polymerized fatty acid, "y" equivalents of diamine such as ethylene diamine, and "z" equivalents of a monofunctional reactant having a secondary amine group as the only reactive functionality. The stoichiometry of the reaction mixture is preferably such that 0.9.ltoreq.{x/(y+z)}.ltoreq.1.1 and 0.1.ltoreq.{z/(y+z)}.ltoreq.0.7. The gel contains about 5-50% tertiary amide terminated polyamide, with the remainder preferably being pure hydrocarbon. The gels are useful in formulating personal care products and other articles wherein some degree of gel-like or self-supporting consistency is desired.

Um peso molecular baixo, amido tertiary polyamide terminado pode ser misturado com um hidrocarboneto líquido para dar forma a uma composição transparente que tem a consistência do gel. Amido tertiary o polyamide terminado pode ser preparado reagir equivalentes de "x" do ácido dicarboxylic wherein ao menos 50% daqueles equivalentes são do ácido fatty polimerizado, equivalentes de "y" do diamine tais como o diamine do etileno, e por equivalentes de "z" de um reactant do monofunctional que tem um grupo secundário do amine como a única funcionalidade reactive. O stoichiometry da mistura de reação é preferivelmente tal que 0.9.ltoreq.{x/(y+z)}.ltoreq.1.1 e 0.1.ltoreq.{z/(y+z)}.ltoreq.0.7. O gel contem amido tertiary o polyamide aproximadamente 5-50% terminado, com o restante preferivelmente que é hidrocarboneto puro. Os gels são úteis em produtos pessoais formulando do cuidado e em outros artigos wherein algum grau de consistência gel-like ou self-supporting é desejado.