Method for obtaining the foamed organosilicon compositions, involving
mixing of organosiloxane rubber (OR), organosilicon joining agent (JA) and
modifier (M). Agents acting like (OR) are represented by
polyorganosiloxane block-copolymers having formula as follows: {[R.sup.1
SiO.sub.1.5 ].sub.a [R.sup.2 (OH)SiO].sub.b, [R.sup.3 R.sup.4 SiO].sub.c
}.sub.n, where: R.sup.1 R.sup.2 R.sup.3 R.sup.4 are aliphatic, aromatic
radicals having from 1 to 6 atoms carbon; n is an integer from 30 to 360;
c=1; a is selected from the 0.019-3.760 interval; b is selected from the
0.008-0.240 interval; or the mixture of the above block-copolymer with the
".alpha.", ".omega."-dihydroxypolydiorganosiloxane in the ratio of
(0.05-0.5):1, respectively; while the individual compositions or mixtures
of polyorganohydridesiloxanes act as (JA), having general formula as
follows: R.sub.3 SiO[R.sup.1 (H)SiO].sub.m --[R.sup.2 SiO].sub.n
SiR.sub.3, or at least one substance from the compositions having general
formula as follows: RSiX.sub.3, where: R=alkyl radical having from 1 to 6
atoms carbon, CH.sub.2.dbd.CH--, X:--ON.dbd.C(CH.sub.3).sub.2,
--OC(O)--CH.sub.3, and amines are used as (M), having general formula as
follows: R.sup.1 R.sup.2 N--(CH.sub.2).sub.n --Si(OR.sup.3).sub.3, or the
mixture of sodium bicarbonate with zinc oxide, or non-organic compound of
cobalt with 34% cobalt content, with the proviso of mass fraction ratio of
(OR) mixed components as follows: (OR)=100; (JA)=from 2 to 15; (M)=from 2
to 22.
Método para obtener las composiciones hechas espuma del organosilicon, implicando mezclarse del caucho del organosiloxane (O), el agente que ensambla del organosilicon (JA) y el modificante (m). Los bloquear-copoli'meros del polyorganosiloxane representan a los agentes que actúan como (O) que tienen fórmula como sigue: {[ R.sup.1 SiO.sub.1.5 ].sub.a [ R.sup.2 (OH)SiO].sub.b, [ R.sup.3 R.sup.4 SiO].sub.c}.sub.n, donde: R.sup.1 R.sup.2 R.sup.3 R.sup.4 son radicales alifáticos, aromáticos que tienen a partir carbón de 1 a 6 átomos; n es un número entero a partir del 30 a 360; c=1; a se selecciona del 0.019-3.760 intervalo; b se selecciona del 0.008-0.240 intervalo; o la mezcla del bloquear-copoli'mero antedicho con el "alpha.", "omega."-dihydroxypolydiorganosiloxane en el cociente de (0.05-0.5):1, respectivamente; mientras que actúan las composiciones o las mezclas individuales de polyorganohydridesiloxanes como (JA), teniendo fórmula general como sigue: R.sub.3 SiO[R.sup.1 (H)SiO].sub.m -- [R.sup.2 SiO].sub.n SiR.sub.3, o por lo menos una sustancia de las composiciones que tienen fórmula general como sigue: RSiX.sub.3, donde: R=alkyl radical teniendo a partir carbón de 1 a 6 átomos, CH.sub.2.dbd.CH --. X: -- ON.dbd.C(CH.sub.3).sub.2, -- OC(O) -- CH.sub.3, y las aminas se utilizan como (m), teniendo fórmula general como sigue: R.sup.1 R.sup.2 N -- (CH.sub.2).sub.n -- Si(OR.sup.3).sub.3, o la mezcla del bicarbonato de sodio con el óxido del cinc, o el compuesto no-orga'nico del cobalto con el contenido del cobalto del 34%, con la claúsula del cociente total de la fracción de (O) mezclaron componentes como sigue: (OR)=100; (JA)=from 2 a 15; (M)=from 2 a 22.