Frangible, spray dried agglomerate catalyst supports are provided, e.g. of silica gel, which possess a controlled morphology of microspheroidal shape, rough, scabrous appearance, and interstitial void spaces which penetrate the agglomerate surface and are of substantially uniform size and distribution. The agglomerates also possess a 1-250 micron particle size, 1-1000 m.sup.2 /gm. surface area, and an Attrition Quality Index (AQI) of at least 10. The agglomerates are derived from a mixture of dry milled inorganic oxide particles, e.g. silica gel, and optionally but preferably wet milled inorganic oxide particles, e.g. silica gel particles, (which preferably contain a colloidal segment of <1 micron particles) slurried in water for spray drying. The high AQI assures that the agglomerates are frangible and that polymerization performance is improved. The controlled morphology is believed to permit the constituent particles of the agglomerates to be more uniformly impregnated or coated with conventional olefin polymerization catalysts.

Las ayudas frangible, secadas a presión de aire del catalizador de la aglomeración se proporcionan, e.g. del gel de silicona, que poseen una morfología controlada de la forma microspheroidal, del aspecto áspero, scabrous, y de los espacios vacíos el intersticial que penetran la superficie de la aglomeración y están de tamaño substancialmente uniforme y de distribución. Las aglomeraciones también poseen un tamaño de partícula del micrón 1-250, un área superficial de 1-1000 m.sup.2 /gm., y un índice de la calidad del agotamiento (AQI) de por lo menos 10. Las aglomeraciones se derivan de una mezcla de las partículas inorgánicas molidas secas del óxido, e.g. el gel de silicona, y mojó opcionalmente pero preferiblemente las partículas inorgánicas molidas del óxido, e.g. las partículas del gel de silicona, (de las cuales contenga preferiblemente un segmento coloidal