A shrink film is provided which is superior in glossiness, mechanical strength, and rigidity, and which is also provided with a property of preventing natural shrinkage. The shrink film with excellent properties is produced by using a resin composition which is obtained by graft polymerization of copolymers of styrene and butadiene with styrene, methylmethacrylate, and butylacrylate. The thus obtained resin composition is extruded after melting and kneading, and drawn into a film in two directions, and exposed at a temperature within a temperature range for the thermal setting so as to obtain the orientation according to ASTM D1504 of the shrink film in range of 1.5 to 5.0 MPa.

Se proporciona una película de encogimiento que es superior en brillo, fuerza mecánica, y rigidez, y que también se proporciona una característica de prevenir la contracción natural. La película de encogimiento con las características excelentes es producida usando una composición de la resina que sea obtenida por la polimerización del injerto de copolímeros del estireno y del butadieno con estireno, methylmethacrylate, y butylacrylate. La composición así obtenida de la resina se saca después de derretir y de amasar, y se dibuja dentro de una película en dos direcciones, y se expone en una temperatura dentro de una gama de temperaturas para la termal que fija para obtener la orientación según ASTM D1504 de la película de encogimiento en la gama de 1.5 a 5.0 MPa.