A relatively small amount of a plasticizer having an SP value of at least 8.8 and a molecular weight of at most 550 is added to blend rubber of NBR-PVC in which NBR has an AN content of from 43 to 50% by weight. The fuel impermeability and the low-temperature flexibility of the resulting rubber composition are improved to be comparable to those of FKM, and the amount of the plasticizer and its reaction product to be released from the rubber composition in fuel is reduced. Adding a controlled amount of carbon black to the rubber composition makes the composition have favorable electroconductivity. The rubber composition is formed into hoses or electroconductive hoses of low fuel permeation.

Verhältnismäßig etwas eines Plastifiziermittels, das einen SP Wert von 8.8 mindestens haben und des Molekulargewichtes von höchstens 550 wird Mischung Gummi von NBR-PVC hinzugefügt, in dem NBR EINEN Inhalt von von 43 bis 50% nach Gewicht hat. Die Kraftstoffundurchlässigkeit und die niedrigtemperaturflexibilität des resultierenden Gummiaufbaus werden verbessert, um mit denen von FKM vergleichbar zu sein, und die Menge des vom Gummiaufbau im Kraftstoff freigegeben zu werden Plastifiziermittels und seines Reaktion Produktes, wird verringert. Das Hinzufügen einer kontrollierten Menge Russes dem Gummiaufbau läßt den Aufbau vorteilhaftes electroconductivity haben. Der Gummiaufbau wird in Schläuche oder in elektrizitätsleitende Schläuche der niedrigen Kraftstoffdurchdringung gebildet.

 
Web www.patentalert.com

< (none)

< Gaseous blend of Ox and its use for biological burden reduction

> Water-swellable crosslinked polymer composition and production

> (none)

~ 00024