A process for manufacture of molten carbonate fuel cell matrices in which an aluminate precursor material and a lithium salt are mixed in an aqueous or organic solvent, resulting in formation of a suspension, the suspension is heated to a temperature less than a boiling of the solvent, resulting in formation of a slurry comprising a lithium aluminate precursor material, at least one casting additive is added to the slurry, the slurry is formed into a desired shape, the desired shape is dried or cured to yield a green molten carbonate fuel cell structure, and the green molten carbonate fuel cell structure is heated after assembly into a molten carbonate fuel cell to the molten carbonate fuel cell operating temperature, resulting in transformation of the lithium aluminate precursor material to lithium aluminate.

Процесс для изготовления жидких матриц топливного элемента карбоната в материал прекурсора алюмината и соль лития смешаны в водяной или органический растворитель, resulting in образование подвеса, подвес нагрет к температуре чем кипеть растворителя, resulting in образование slurry состоя из материала прекурсора алюмината лития, по крайней мере одна бросая добавка добавлен к slurry, slurry сформирован в заданную форму, заданная форма высушена или вылечена для того чтобы произвести зеленую жидкую структуру топливного элемента карбоната, и зеленая жидкая структура топливного элемента карбоната нагрета после агрегата в жидкий топливный элемент карбоната жидкая рабочая температура топливного элемента карбоната, resulting in преобразование материала прекурсора алюмината лития к алюминату лития.