Phenylethynyl containing reactive additives were prepared from aromatic diamines containing phenylethynyl groups and various ratios of phthalic anhydride and 4-phenylethynylphthalic anhydride in glacial acetic acid to form the imide in one step or in N-methyl-2-pyrrolidinone to form the amide acid intermediate. The reactive additives were mixed in various amounts (10% to 90%) with oligomers containing either terminal or pendent phenylethynyl groups (or both) to reduce the melt viscosity and thereby enhance processability. Upon thermal cure, the additives react and become chemically incorporated into the matrix and effect an increase in crosslink density relative to that of the host resin. This resultant increase in crosslink density has advantageous consequences on the cured resin properties such as higher glass transition temperature and higher modulus as compared to that of the host resin.

Phenylethynyl, das reagierende Zusätze enthält, wurden aus den aromatischen Diaminen vorbereitet, die phenylethynyl Gruppen und verschiedene Verhältnisse des Phthal- Anhydrids und des Anhydrids 4-phenylethynylphthalic in der Glazial- Essigsäure enthalten, um das Imid in einem Schritt oder in N-methyl-2-pyrrolidinone zu bilden, um den sauren Vermittler des Amids zu bilden. Die reagierenden Zusätze wurden in den verschiedenen Mengen (10% bis 90%) mit den Oligomeren enthalten entweder am Ende oder pendent phenylethynyl Gruppen (oder beide) um die Schmelzviskosität zu verringern und processability dadurch zu erhöhen gemischt. Nach thermischer Heilung reagieren die Zusätze und werden chemisch in die Matrix verbunden und bewirken eine Zunahme der relative.to Querverbindungdichte das des Wirt Harzes. Diese resultierende Zunahme der Querverbindungdichte hat vorteilhafte Konsequenzen auf den kurierten Harzeigenschaften wie höherer Glasübergangstemperatur und höherem Modul verglichen mit der des Wirt Harzes.