Disclosed are (1) a titania-zirconia powder having at least a part of the zirconia solid-dissolved in the titania crystalline phase or at least a part of the titania solid-dissolved in the zirconia crystalline phase, (2) a titania-zirconia powder containing 3 to 30 wt % of zirconia and 0.5 to 10 wt % of yttria and containing less than 20 wt %, in total, of at least a complex oxide having a composition of ZrTiO.sub.4 or (Ti,Zr) O.sub.2, monoclinic phase zirconia, and tetragonal phase zirconia, wherein the titania-zirconia powder comprises an anatase phase, and which retains a specific surface area of 34 m.sup.2 /g or more after heat-treated at 900.degree. C. for 5 hours in the air, and (3) a titania-zirconia powder wherein the titania-zirconia powder (1) or (2) having an average particle size of 1 .mu.m or smaller is mutually dispersed with an alumina powder; and processes for producing the powders are disclosed.

Αποκαλύπτεται (1) μια σκόνη titania-zirconia που έχει τουλάχιστον ένα μέρος του zirconia στερεός-που διαλύεται στην κρυστάλλινη φάση titania ή τουλάχιστον ένα μέρος του titania στερεός-που διαλύεται στην κρυστάλλινη φάση zirconia, (2) μια σκόνη titania-zirconia που περιέχει 3 έως 30 wt% του zirconia και 0,5 έως 10 wt% του yttria και που περιέχει λιγότερο από 20 βάρος %, στο σύνολο, τουλάχιστον ενός σύνθετου οξειδίου που έχει μια σύνθεση ZrTiO.sub.4 ή (Tj, zr) O.sub.2, του μονοκλινικού zirconia φάσης, και του tetragonal zirconia φάσης, όπου η σκόνη titania-zirconia περιλαμβάνει μια φάση anatase, και που διατηρεί μια συγκεκριμένη περιοχή επιφάνειας 34 m.sup.2/toy γ ή περισσότεροι μετά από υποβαλλόμενο σε θερμοθεραπεία σε 900.degree. Γ. για 5 όπου η σκόνη titania-zirconia (1) ή (2) που έχει ένα μέσο μέγεθος μορίων 1 μu.μ ή μικρότερος είναι αμοιβαία διασκορπισμένη με μια σκόνη αλουμίνας και οι διαδικασίες για τις σκόνες αποκαλύπτονται.