Ultrafine particulates of highly white zinc oxide having a reduced average particle diameter of about 15 nm to about 55 nm as measured by the BET-one point method and that has an L value of about 90 or more as measured by a Hunter-type color-difference meter. Also, a process for producing ultrafine particulates of highly white zinc oxide, comprising oxidizing zinc vapor with an oxidizing gas in a reactor, wherein a zinc vapor-containing gas has a temperature of about 950.degree. C. or more at a nozzle of the reactor for discharging the zinc vapor-containing gas and the oxidizing gas has a temperature of about 900.degree. C. or more at a nozzle of the reactor for discharging the oxidizing gas is disclosed.

Os particulates de Ultrafine do óxido altamente branco do zinco que tem um diâmetro médio reduzido da partícula de aproximadamente 15 nm a aproximadamente 55 nm como medido pelo Apostaramque método e aquele do ponto tem um L valor de aproximadamente 90 ou mais como medido por um Caçador-tipo medidor da cor-diferença. Também, um processo para produzir os particulates do ultrafine do óxido altamente branco do zinco, compreendendo o vapor de oxidação do zinco com um gás de oxidação em um reator, wherein um gás vapor-contendo do zinco tem uma temperatura aproximadamente de 950.degree. O C. ou mais em um bocal do reator para descarregar o gás vapor-contendo do zinco e o gás de oxidação têm uma temperatura aproximadamente de 900.degree. O C. ou mais em um bocal do reator para descarregar o gás de oxidação são divulgados.