A non-carbon, metal-based slow-consumable anode of a cell for the electrowinning of aluminium self-forms during normal electrolysis an electrochemically-active oxide-based surface layer (20). The rate of formation (35) of the layer (20) is substantially equal to its rate of dissolution (30) at the surface layer/electrolyte interface (25) thereby maintaining its thickness substantially constant, forming a limited barrier controlling the oxidation rate (35). The anode (10) usually comprises an alloy of iron with at least one of nickel, copper, cobalt or zinc which during use forms an oxide surface layer (20) mainly containing ferrite.

Нон-uglerod, металл-osnovanny1 медленн-potrebl4emy1 анод клетки для electrowinning собственн-form алюминия во время нормального электролиза электрохимическ-aktivno окис-osnovanny1 поверхностный слой (20). Тариф образования (35) слоя (20) существенн равн к своему тарифу растворения (30) на поверхности стыка поверхности layer/electrolyte (25) таким образом поддерживая свою толщину существенн постоянн, формируя лимитированный барьер контролируя тариф оксидации (35). Анод (10) обычно состоит из сплава утюга с по крайней мере одним из никеля, меди, кобальта или цинка который во время форм пользы слой окиси поверхностный (20) главным образом содержа феррит.

 
Web www.patentalert.com

< (none)

< Fuel-cell engine stream conditioning system

> Comparative phenotype analysis for assessment of biologically active compounds such as antimicrobials

> (none)

~ 00042