Adhesive tape backings comprising isotactic polypropylene blended or mixed with at least a second polyolefin. The backing is biaxially stretched so as to provide a film having any one or a combination of the following preferred characteristics: A. Puncture energy up to 20 J/cm.sup.2 when 2.54 cm wide samples are tested by the method set herein, or up to 90 J/cm.sup.2 when 1.27 cm wide samples are tested by the method set out herein. B. Puncture elongation up to about 1.3 cm when 2.54 cm wide samples are tested by the method set out herein, or up to 2.0 cm when 1.27 cm wide samples are tested by the method set out herein. C. Tensile strength up to 140 MPa in the MD. In a preferred embodiment, the second component comprises polyethylene, polybutylene, or syndiotactic polypropylene.

Os revestimentos protetores da fita adesiva adesiva que compreendem o polypropylene isotactic misturaram-se ou misturaram-se com ao menos um segundo polyolefin. O revestimento protetor é esticado biaxially para fornecer uma película que têm algum ou uma combinação das seguintes características preferidas: A. Puncione a energia até 20 J/cm.sup.2 quando as amostras de 2.54 cm de largura são testadas pelo método ajustado nisto, ou até 90 J/cm.sup.2 quando as amostras de 1.27 cm de largura são testadas pelo método ajustado para fora nisto. B. Puncione o elongation até aproximadamente 1.3 cm quando as amostras de 2.54 cm de largura são testadas pelo método ajustado para fora nisto, ou até 2.0 cm quando as amostras de 1.27 cm de largura são testadas pelo método ajustado para fora nisto. C. Força tensile até 140 MPa no MD. Em uma incorporação preferida, o segundo componente compreende o polietileno, o polybutylene, ou o polypropylene syndiotactic.

 
Web www.patentalert.com

< (none)

< Antisense modulation of CHK2 expression

> Piston pump

> (none)

~ 00045