A non-chrome, copper-containing catalyst, Cu--Al--O and method of preparing the same are provided wherein the Cu--Al--O catalyst is prepared by the co-precipitation of copper nitrate (Cu(NO.sub.3).sub.2) and sodium aluminate (Na.sub.2 Al.sub.2 O.sub.4) solutions using sodium carbonate (Na.sub.2 CO.sub.3) as a precipitant. the precipitate is filtered, washed to remove excess sodium, and dried. The dried product, to be used in a powder form, is calcined at a preferred temperature of approximately 700 to 900.degree. C. for approximately 1 to 4 hours. The dry powder, to be tableted or extruded, is calcined at a temperature of approximately 400 to 700.degree. C. The activity of the Cu--Al--O catalyst can be promoted in hydrogenolysis applications by the addition of various agents. The Cu--Al--O catalyst can be employed in applications in place of Cu/Cr, or other copper-based catalysts.

Un no-cromo, cobre-conteniendo el catalizador, el Cu -- al -- O y el método de preparar igual se proporcionan en donde el Cu -- al -- catalizador de O es preparado por la co-precipitacio'n de las soluciones de cobre del nitrato (Cu(NO.sub.3).sub.2) y del aluminato del sodio (Na.sub.2 Al.sub.2 O.sub.4) usando el carbonato de sodio (Na.sub.2 CO.sub.3) como se filtra un precipitado el precipitado, lavado para quitar exceso de sodio, y secado. El producto secado, ser utilizado en una forma del polvo, se calcina en una temperatura preferida de aproximadamente 700 a 900.degree. C. por aproximadamente 1 a 4 horas. El polvo seco, ser marcado en la tableta o ser sacado, se calcina en una temperatura de aproximadamente 400 a 700.degree. C. La actividad del Cu -- al -- catalizador de O se puede promover en usos del hydrogenolysis por la adición de varios agentes. El Cu -- al -- catalizador de O se puede emplear en usos en lugar de Cu/Cr, u otro cobre-baso' los catalizadores.