A free-machining, precipitation-hardenable, martensitic stainless steel is described that provides a unique combination of machinability, processability, and toughness. The broad compositional range of the steel alloy of the invention is as follows, in weight percent:

                    C                  0.030 max.
                    Mn                 0.75 max.
                    Si                 0.75 max..
                    P                  0.040 max.
                    S                  0.15-0.35
                    Cr                 14.0-15.5
                    Ni                  5.0-6.0
                    Mo                 0.50-1.2
                    Cu                  3.0-4.0
                    Nb                 0.10-0.30
                    B                  0.010 max.
                    N                  0.030 max.

The balance of the alloy is iron and the usual impurities found in commercial grades of martensitic precipitation-hardening stainless steels intended for similar use or service.

Μια ελεύθερος-κατεργασία, πτώση-χαρδεναψλε, μαρτενσιτικός ανοξείδωτος χάλυβας περιγράφεται που παρέχει έναν μοναδικό συνδυασμό κατασκευασιμότητας, δυνατότητας επεξεργασίας, και ανθεκτικότητας. Η ευρεία συνθετική σειρά του κράματος χάλυβα της εφεύρεσης είναι η ακόλουθη, στα τοις εκατό βάρους: Γ 0,030 ανώτατο. ΜΝ 0,75 ανώτατο. Θ*Ση 0,75 ανώτατο .. Π 0,040 ανώτατο. Θ*ς 0.15-0.35 χρώμιο 14.0-15.5 Νι 5.0-6.0 MO 0.50-1.2 cu 3.0-4.0 NB 0.10-0.30 β 0,010 ανώτατο. Ν 0,030 ανώτατο. Η ισορροπία του κράματος είναι σίδηρος και οι συνηθισμένες ακαθαρσίες που βρίσκονται στους εμπορικούς βαθμούς μαρτενσιτικών πτώση-σκληραίνοντας ανοξείδωτων χαλύβων προοριζόμενων για την παρόμοια χρήση ή την υπηρεσία.