This invention discloses a process for devulcanizing the surface of
reclaimed rubber crumb into surface devulcanized reclaimed rubber crumb
that is suitable for being recompounded and recurred into high performance
rubber products, said process comprising the steps of (1) heating the
reclaimed rubber crumb to a temperature within the range of about
150.degree. C. to about 300.degree. C. under pressure of at least about
3.4.times.10.sup.6 Pascals in the presence of 2-butanol to devulcanized
the surface of the rubber crumb thereby producing a slurry of the surface
devulcanized reclaimed rubber crumb in the 2-butanol, wherein the
reclaimed rubber crumb has a particles size which is within the range of
about 325 mesh to about 20 mesh, and (2) separating the surface
devulcanized reclaimed rubber crumb from 2-butanol.
Deze uitvinding onthult een proces om de oppervlakte van teruggewonnen rubberkruimel in oppervlakte devulcanizing teruggewonnen rubberkruimel devulcanized die geschikt is om te zijn recompounded en terugkwam in hoge prestaties rubberproducten, devulcanized het bovengenoemde proces dat uit de stappen van (1) het verwarmen van de teruggewonnen rubberkruimel aan een temperatuur binnen de waaier van ongeveer 150.degree. C. aan 300.degree. C. onder druk van op zijn minst over 3.4.times.10.sup.6 Pascal in aanwezigheid van 2-butanol bestaat aan ongeveer de oppervlakte van de rubberkruimel daardoor devulcanized het produceren van een dunne modder van de oppervlakte teruggewonnen rubberkruimel in het 2-butanol, waarin de teruggewonnen rubberkruimel een deeltjesgrootte heeft die binnen de waaier van ongeveer netwerk 325 aan netwerk ongeveer 20 is, en (2) scheidend into surface devulcanized reclaimed rubber crumb that is suitable for being recompounded and recurred into high performance rubber products, said process comprising the steps of (1) heating the reclaimed rubber crumb to a temperature within the range of about 150.degree. C. to about 300.degree. C. under pressure of at least about 3.4.times.10.sup.6 Pascals in the presence of 2-butanol to devulcanized the surface of the rubber crumb thereby producing a slurry of the surface devulcanized reclaimed rubber crumb in the 2-butanol, wherein the reclaimed rubber crumb has a particles size which is within the range of about 325 mesh to about 20 mesh, and (2) separating the surface devulcanized teruggewonnen rubberkruimel van 2-butanol.