Brake disc produced by a hot-rolled stainless steel excellent in resistance
to temper softening, characterized in that: said steel contains, in terms
of wt %, C: 0.01 to 0.1%, N: 0.03% or less, C+N: 0.04 to 0.1%, Si: 1% or
less, Mn: 20 or less, Ni: less than 0.5%, Cr: 10 to 15%, and Nb: 0.02% to
0.5%, with the balance Fe and unavoidable impurities; that the hardness
after quenching heat treatment is in the range of 30 to 40 HRC; and that
the temper softening temperature for lowering the hardness to below 30 HRC
is at least 530.degree. C. Further, it is desirable to add at least one of
the following elements; 0.1 to 2% of Cu, 0.1 to 1% of Mo, 0.01 to 0.5% of
Ti, 0.01 to 0.5% of V or 0.0005 to 0.01% of B, and to make the value of
.gamma..sub.p calculated from steel chemical composition at least 70%.
Freie o disco produzido por um aço inoxidável hot-rolled excelente na resistência para moderar amaciar, caracterizado naquele: o aço dito contem, nos termos do peso %, C: 0.01 a 0.1%, N: 0.03% ou menos, C+N: 0.04 a 0.1%, silicone: 1% ou menos, manganês: 20 ou menos, Ni: menos de 0.5%, cr: 10 a 15%, e Nb: 0.02% a 0.5%, com o Fe do contrapeso e as impurezas unavoidable; que a dureza após ter extinguido o tratamento de calor está na escala de 30 a 40 HRC; e que a temperatura amaciando da têmpera para abaixar a dureza a abaixo 30 HRC é ao menos 530.degree. C. Mais mais, é desejável adicionar ao menos um dos seguintes elementos; 0.1 a 2% do cu, 0.1 a 1% do Mo, 0.01 a 0.5% do ti, 0.01 a 0.5% de V ou 0.0005 a 0.01% de B, e para fazer o valor do gamma..sub.p calcularam da composição química de aço ao menos 70%.