The present invention relates to glass ceramic material and its use as
means for joining different types of material and as support. Said glass
ceramic material comprising, on a weight percent basis, 10-35% MgO, 10-55%
BaO and 25-50% SiO.sub.2 and is formed by the following steps: a) melting
of glass raw material at a temperature in excess of 1450 .degree. C. and
that the thereby formed melt is cooled rapidly to a temperature below
900.degree. C. and thereafter to ambient temperature to form a precursor
glass, b) milling of the precursor glass into a sinterable glass powder
with an average particle size in the range of 1 micron to 100 microns, c)
forming of the glass powder into a green body of suitable shape, with or
without organic processing aids, and subjecting said green body to a
thermal treatment comprising a heating stage of average heating rate not
exceeding 100 .degree. C./minute between the temperatures of 750 .degree.
C. and 900 .degree. C.
Присытствыющий вымысел относит к стеклянному керамическому материалу и своей пользе как середины для соединять по-разному типы материала и как поддержка. Сказанное стеклянное керамическое материальное состоящ из, на основание процентов веса, 10-35% mgO, 10-55% BaO и 25-50% SiO.sub.2 и сформировано following шагами: a) плавить стеклянный сыройа материал на температуре свыше degree 1450. C и то таким образом сформированный melt охлажены быстро к температуре под 900.degree. C и в дальнейшем к окружающей температуре для того чтобы сформировать стекло прекурсора, филировать б) стекла прекурсора в sinterable стеклянный порошок с средним размером частицы в ряде 1 микрона к 100 микронов, формировать ч) стеклянного порошка в зеленое тело целесообразной формы, с или без органической обрабатывая помощи, и подвергая сказанного зеленого тела к термально обработке состоя из этапа топления среднего тариффа на отопление не превышая degree 100. C./minute между температурами degree 750. C и degree 900. Ч.