High molybdenum, corrosion-resistant alloys are provided with greatly increased thermal stability by controlling the atom concentrations to be Ni.sub.a Mo.sub.b X.sub.c Y.sub.d Z.sub.e, where: a is between about 73 and 77 atom percent b is between about 18 and 23 atom percent X is one or more required substitutional alloying elements selected from Groups VI, VII and VIII of the Periodic Table and c does not exceed about 5 atom percent for any one element, Y is one or more optional substitutional alloying elements which may be present and d does not exceed about one atom percent for any one element, Z is one or more interstitial elements and e is as low as possible, not exceeding about 0.2 atom percent in total; and the sum of c and d is between about 2.5 and 7.5 atom percent.

Высокий молибден, коррозионностойкие сплавы обеспечен с больш увеличенной термально стабилностью путем контролировать концентрацию атома для того чтобы быть Ni.sub.a Mo.sub.b X.sub.c Y.sub.d Z.sub.e, где: а находится между около 73 и 77 процентами б атома находит между около 18 и 23 процентами x атома будет one or more необходимо substitutional сплавлять элементами выбранными от групп VI, VII и VIII из периодическаяа таблица и ч не превышают около 5 процентов атома для любого одного элемента, ы будет one or more опционные substitutional сплавляя элементы которые могут присутствовать и д не превышает около один процент атома для любого одного элемента, з будет one or more внутрипоровые элементы и е как можно низок, превышающ около 0.2 процента атома в итоге; и сумма ч и д находится между около 2.5 и 7.5 процентами атома.