The present invention includes lithium manganese oxide spinel compounds
having a low porosity, a high tap density and a high pellet density, and
methods of preparing these compounds. In particular, the method comprises
preparing a lithium manganese oxide with a spinel structure and having the
formula: wherein:
Li.sub.1+X Mn.sub.2-Y M.sub.m.sub..sub.1 .sup.1 M.sub.m.sub..sub.2 .sup.2 .
. . M.sub.m.sub..sub.k .sup.k O.sub.4+Z
M.sup.1, M.sup.2, . . . M.sup.k are cations different than lithium or
manganese selected from the group consisting of alkaline earth metals,
transition metals, B, Al, Si, Ga and Ge;
X, Y, m.sub.1, m.sub.2, . . . , m.sub.k, each have a value between 0 and
0.2;
Z has a value between -0.1 and 0.2; and
X, Y, m.sub.1, m.sub.2, . . . m.sub.k are selected to satisfy the equation:
Y=X+m.sub.1 +m.sub.2 + . . . +m.sub.k.
La presente invenzione include i residui spinel dell'ossido del manganese del litio che hanno una porosità bassa, un'alta densità del colpetto e un'alta densità della pallina e metodi di preparazione dei questi residui. In particolare, il metodo contiene la preparazione dell'ossido del manganese del litio con una struttura spinel ed avere la formula: in cui: Sup.2 del sup.1 M.sub.m.sub..sub.2 di Li.sub.1+X Mn.sub.2-Y M.sub.m.sub..sub.1. . . Sup.k O.sub.4+Z M.sup.1, M.sup.2 di M.sub.m.sub..sub.k. . . M.sup.k sono cationi differenti che il litio o il manganese scelto dal gruppo che consiste dei metalli della terra alcalina, dei metalli di transizione, della B, di Al, del silicone, di Ga e del GE; X, Y, m.sub.1, m.sub.2. . . , m.sub.k, ciascuno hanno un valore fra 0 e 0.2; La Z ha un valore fra -0.1 e 0.2; e X, Y, m.sub.1, m.sub.2. . . m.sub.k sono selezionati per soddisfare l'equazione: Y=X+m.sub.1 +m.sub.2 +. . . +m.sub.k.