Substantially linear olefin polymers having a melt flow ratio, I.sub.10 /I.sub.2, .gtoreq.5.63, a molecular weight distribution, M.sub.w /M.sub.n, defined by the equation: M.sub.w /M.sub.n.ltoreq.(I.sub.10 /I.sub.2)-4.63, and a critical shear stress at onset of gross melt fracture of greater than about 4.times.10.sup.6 dyne/cm.sup.2 and their method of manufacture are disclosed. The substantially linear olefin polymers preferably have at least about 0.01 long chain branches/1000 carbons and a molecular weight distribution from about 1.5 to about 2.5. The new polymers have improved processability over conventional olefin polymers and are useful in producing fabricated articles such as fibers, films, and molded parts.

Polimeri sostanzialmente lineari dell'olefina che hanno un rapporto di flusso della fusione, I.sub.10 /I.sub.2, gtoreq.5.63, una distribuzione del peso molecolare, M.sub.w /M.sub.n, definito dall'equazione: M.sub.w /M.sub.n.ltoreq.(I.sub.10 /I.sub.2)-4.63 e una sollecitazione di taglio critica all'inizio della frattura lorda della fusione di più grande di circa 4.times.10.sup.6 dyne/cm.sup.2 ed il loro metodo della fabbricazione sono rilevati. I polimeri sostanzialmente lineari dell'olefina hanno preferibilmente almeno circa 0.01 carbonio a lunga catena branches/1000 e una distribuzione del peso molecolare da circa 1.5 a circa 2.5. I nuovi polimeri hanno migliorato i polimeri convenzionali dell'olefina dell'eccedenza di processability e sono utili nel produrre gli articoli fabbricati quali le fibre, le pellicole e le parti modellate.