The present application describes a porous polymethylsilsesquioxane (PMS) having a specific surface area between approximately 50 m.sup.2 /g and 500 m.sup.2 /g, a pore volume between approximately 0.1 cm.sup.3 /g and 0.8 cm.sup.3 /g, a monolayer volume between approximately 10 cm.sup.3 /g and 60 cm.sup.3 /g, a pore radius smaller than 1 nm for 90% of the pores and insolubility in water and organic solvents. The PMS according to the invention is prepared by precipitation of a polymethylsiliconate of the general formula ##STR1## in which n is a whole number between approximately 20 and 100 and M is an alkaline metal or alkaline-earth metal or NH.sub.4.sup.+.

Η παρούσα εφαρμογή περιγράφει ένα πορώδες polymethylsilsesquioxane (PMS) που έχει μια συγκεκριμένη περιοχή επιφάνειας μεταξύ περίπου 50 m.sup.2/g και 500 m.sup.2/g, ενός όγκου πόρων μεταξύ περίπου 0,1 cm.sup.3/g και 0,8 cm.sup.3/g, ενός monolayer όγκου μεταξύ περίπου 10 cm.sup.3/toy γ και 60 cm.sup.3/toy γ, μια ακτίνα πόρων μικρότερη από 1 NM για 90% των πόρων και insolubility στο ύδωρ και τους οργανικούς διαλύτες. Το PMS σύμφωνα με την εφεύρεση προετοιμάζεται από την πτώση ενός polymethylsiliconate του γενικού τύπου ## STR1 ## στον οποίο το ν είναι ακέραιος ένας αριθμός μεταξύ περίπου 20 και 100 και το μ είναι ένα αλκαλικό μέταλλο ή αλκαλικών γαιών μέταλλο ή NH.sub.4.sup. +.