A duplex stainless steel including, in weight percent, up to 0.06 percent
carbon, 15 up to less than 25 percent chromium, greater than 3 up to 6
percent nickel, up to 3.75 percent manganese, 0.14 up to 0.35 percent
nitrogen, up to 2 percent silicon, greater than 1.4 up to less than 2.5
percent molybdenum, up to less than 0.5 percent copper, up to less than
0.2 percent cobalt, up to 0.05 percent phosphorous, up to 0.005 percent
sulfur, and 0.001 up to 0.0035 percent boron, with the remainder being
iron and incidental impurities is disclosed. The duplex stainless steel
may be included in an article of manufacture, such as a strip, bar, plate,
sheet, casting, tubing or piping. A method for making such a duplex
stainless steel is also disclosed.
Ein rostfreier Duplexstahl einschließlich, in den Gewichtprozenten, in bis 0.06 Prozent des Carbons, 15 bis bis weniger als 25 Prozent Chrom, bis grösser als 3 bis 6 Prozent Nickel, bis bis 3.75 Prozent Mangan, bis 0.14 bis 0.35 Prozent Stickstoff, bis bis 2 Prozent Silikon, grösser als zu 1.4 bis zu weniger als 2.5 Prozent Molybdän, bis zu weniger als 0.5 Prozent Kupfer, bis bis weniger als 0.2 Prozent Kobalt, bis den phosphorigen, bis 0.005 Prozent von bis 0.05 Prozent Schwefel und zu 0.001 bis 0.0035 Prozent Bor, wenn der Rest Eisen und beiläufige Verunreinigungen ist, wird freigegeben. Der rostfreie Duplexstahl kann in einem Artikel der Herstellung, wie ein Streifen, ein Stab, eine Platte, ein Blatt, ein Gußteil, ein Schläuche oder eine Rohrleitung eingeschlossen werden. Eine Methode für das Bilden solch eines rostfreien Duplexstahls wird auch freigegeben.