In a galvanic solid cell, for example of the Na/SbCl.sub.3 systems, the cathode space is occupied by a self-supporting porous sinter framework of solid electrolyte material, in whose pores the active cathode material is retained. A porous structure can be united with the massive solid electrolyte-separator into a unitary sinter composite of high ion conductivity, to which, if desired, there can also be joined on the anode side a porous sinter framework for receiving the alkali metal. The meltable active electrode materials are introduced by immersion into the porous portions of the sinter composite. The porous solid electrolyte structure can also be used advantageously as the separator system for cells with molten liquid electrodes, e.g. of the Na/S high temperature cell type.

In einer galvanischen festen Zelle z.B. der Systeme Na/SbCl.sub.3, wird der Kathode Raum durch einen selbsttragenden porösen Sinterrahmen des festen Elektrolytmaterials besetzt, in dessen Poren das aktive Kathode Material behalten wird. Eine poröse Struktur kann mit dem massiven festen Elektrolyt-Separator in eine einheitliche Sinterzusammensetzung der hohen Ionenleitfähigkeit vereinigt werden, zu der, wenn es gewünscht wird, dort auf der Anode Seite auch verbunden werden können ein poröser Sinterrahmen für das Empfangen des Alkalimetalls. Die schmelzbaren aktiven Elektrode Materialien werden durch Immersion in die porösen Teile der Sinterzusammensetzung eingeführt. Die poröse feste Elektrolytstruktur kann als das Separatorsystem für Zellen mit flüssigen flüssigen Elektroden, z.B. der Na/S Hochtemperaturzelle Art auch vorteilhaft benutzt werden.

 
Web www.patentalert.com

< (none)

< Hydrogen selenide treatment of electrolytes

> Etched beta"-alumina ceramic electrolyte

> (none)

~ 00070