There is provided a steel of working-induced martensitic type steel consisting essentially, by mass, of 0.01 to 0.10% carbon, not more than 3.0% silicon, more than 5.0 but not more than 10.0% manganese, 1.0 to 12.0% nickel, 4 to 18% chromium, at least one kind of 0.1 to 4.0% in total in terms of Mo +1/2 W which at least one kind is selected from the group consisting of molybdenum and tungsten, from 0 inclusive but not more than 5.0% copper, from 0 inclusive but not more than 0.15% nitrogen, not more than 0.10% aluminum, not more than 0.005% oxygen, and the balance substantially iron, "A" value, which is defined by "A"=Ni+0.65Cr+0.98Mo+0.49W+1.05Mn+0.35Si+Cu+12.6(C+N) (1) with a proviso that any element which is not added is calculated as zero, being in a range of 13 to 27%, said steel containing in austenite a martensite phase of not less than 30 volume % after cold working.

Wird einen Stahl der arbeiten-verursachten martensitic Art der Stahl zur Verfügung gestellt, der im Wesentlichen, von der Masse, von 0.01 bis 0.10% Carbon, nicht mehr Silikon als 3.0%, mehr als 5.0 aber nicht mehr Mangan als 10.0%, Nickel 1.0 bis 12.0%, 4 bis 18% das Chrom, mindestens eine Art von 0.1 bis 4.0% in der Gesamtmenge in MO +1/2 W ausgedrückt besteht, das mindestens eine Art von der Gruppe vorgewählt wird, die im wesentlichen aus Molybdän und Wolfram besteht, von 0 einschließlich aber nicht mehr von Kupfer als 5.0%, von 0 einschließlich aber von nicht mehr als 0.15% Stickstoff, nicht mehr als 0.10% Aluminium, nicht mehr als 0.005% Sauerstoff und das Balance Eisen, "A" Wert, der durch "A"=Ni+0.65Cr+0.98Mo+0.49W+1.05Mn+0.35Si+Cu+12.6(C+N) (1) mit einem Vorbehalt definiert wird, daß irgendein Element, das nicht addiert wird, wird als null errechnet, seiend in einer Strecke 13 bis 27%, besagter Stahl, der im austenite ein martensite Phase von nicht weniger als 30 Volumen % nach kalter Funktion enthält.