The present invention provides a method of manufacturing calcium phosphate powder comprising the steps of preparing a mixed material by mixing calcium hydroxide (Ca(OH).sub.2) powder and calcium hydrogenphosphate powder so that a molar ratio (Ca/P) of calcium to phosphor is set to a range of 1.45-1.72; conducting a mixing/milling treatment to the mixed material to cause a soft-mechanochemical compositing reaction thereby to prepare a calcium phosphate precursor; and conducting a heat treatment to thus obtained precursor at a temperature of 600.degree. C. or more thereby to prepare calcium phosphate powder. According to the present invention, the manufacturing process is simple and the manufacturing cost can be remarkably reduced. In addition, fine calcium phosphate powder excellent in characteristics can be easily manufactured in a short time.

Η παρούσα εφεύρεση παρέχει μια μέθοδο τη σκόνη φωσφορικού άλατος ασβεστίου περιλαμβάνοντας τα βήματα της προετοιμασίας ενός μικτού υλικού με τη μίξη της σκόνης υδροξειδίου ασβεστίου (Ca(OH).sub.2) και της σκόνης ασβεστίου hydrogenphosphate έτσι ώστε μια μοριακή αναλογία (Ca/P) του ασβεστίου στο φωσφόρο τίθεται μια σειρά 1.45-1.72 διευθύνοντας μια επεξεργασία μίξης/άλεσης στο μικτό υλικό για να αναγκάσει μια μαλακός- mechanochemical compositing αντίδραση με αυτόν τον τρόπο για να προετοιμάσει έναν πρόδρομο φωσφορικού άλατος ασβεστίου και διευθύνοντας μια θερμική επεξεργασία στον έτσι αποκτηθέντα πρόδρομο σε μια θερμοκρασία 600.degree. Γ. ή περισσότερο με αυτόν τον τρόπο για να προετοιμάσει τη σκόνη φωσφορικού άλατος ασβεστίου. Σύμφωνα με την παρούσα εφεύρεση, η διαδικασία κατασκευής είναι απλή και το κόστος παραγωγής μπορεί να μειωθεί εντυπωσιακά. Επιπλέον, η λεπτή σκόνη φωσφορικού άλατος ασβεστίου άριστη στα χαρακτηριστικά μπορεί να κατασκευαστεί εύκολα σε σύντομο χρονικό διάστημα.