The present invention relates to a continuous electrochemical process for preparing zinc powder. The process involves providing to an electrochemical cell a suspension in a 1.25 Molar to 10.0 Molar aqueous alkaline solution of zinc oxide or any other zinc compound that reacts with an aqueous alkaline solution to produce zinc oxide, such that the solution or suspension comprises at least 2 millimoles of solubilized zinc based species per 100 grams of electrolyte. Current is passed to the cell at a current density of about 500 to 40,000 A/m.sup.2, for a time period sufficient to electrochemically reduce the solubilized zinc based species to zinc powder, while continuously or intermittently adding a sufficient amount of the zinc oxide or the other zinc compound to the cell to maintain the concentration of the solubilized zinc based species at a level of at least 2 millimoles per 100 grams of electrolyte.

Die anwesende Erfindung bezieht auf einem ununterbrochenen elektrochemischen Prozeß für das Vorbereiten des Zinkpuders. Der Prozeß bezieht mit ein, zu einer elektrochemischen Zelle eine Aufhebung zur Verfügung zu stellen in einen Molar 1.25 zu molarer wäßriger alkalischer Lösung 10.0 des Zinkoxids oder irgendeines anderen Zinkmittel, das mit einer wäßrigen alkalischen Lösung zum Erzeugniszinkoxid reagiert, so, daß die Lösung oder die Aufhebung mindestens 2 millimoles von solubilized Zink gegründeten Sorten pro 100 Gramm des Elektrolyts enthält. Strom wird zur Zelle an einer spezifischen Stromdichte von ungefähr 500 bis 40.000 A/m.sup.2 geführt, denn ein Zeitabschnitt, der genügend ist, das solubilized Zink elektrochemisch zu verringern, gründete Sorte zinc Puder, während eine genügende Menge des Zinkoxids oder des anderen, Zinkmittel der Zelle ununterbrochen oder stoßweise, hinzufügend, um die Konzentration des solubilized Zinks beizubehalten Sorte auf einem Niveau von mindestens 2 millimoles pro 100 Gramm des Elektrolyts gründete.