The present invention relates to a self-baking electrode for use in low
electric reduction furnaces, and refers particularly to a container (1)
for the formation of self-baking electrodes to be used in low electric
reduction furnaces, allowing the manufacture of silicon alloys with iron
content as low as 0.25%, The container comprising an aluminum cylindrical
casing (11) split in two parts containing therein a plurality of stainless
steel ribs (12) uniformly attached perpendicularly along the inner surface
of the casing (11) lengthwise along the cylindrical casing (11), wherein
the cylindrical casing (11) is made of aluminum plates and the ribs (12)
are made of stainless steel plates.
De onderhavige uitvinding heeft op een zelf-bakt elektrode voor gebruik in lage elektrische verminderingsovens betrekking, en verwijst in het bijzonder naar een container (1) voor de vorming van zelf-bakt elektroden die in lage elektrische verminderingsovens moeten worden gebruikt, toestaand de vervaardiging van siliciumlegeringen met ijzerinhoud zo laag zoals 0,25%, de container die uit een spleet van het aluminium cilindrische omhulsel (11) in twee delen bestaan die daarin een meerderheid van roestvrij staalribben (12) bevatten in de lengte loodrecht uniform in bijlage langs de binnenoppervlakte van omhulsel (11) langs cilindrisch omhulsel (11), waarin cilindrisch omhulsel (11) van aluminiumplaten en ribben (12) wordt gemaakt van roestvrij staalplaten worden gemaakt.