Flux cored wire for dual stainless steel having flux filled into a
stainless steel sheath of the invention, the flux contains, with respect
to the total weight of the wire: 0.02 to 0.10 wt % C; 0.10 to 1.0 wt % Si;
1.0 to 3.0 wt % Mn, 15 to 35 wt % Cr, 7.0 to 12.0 wt % Ni; 1.5 to 3.5 wt %
Mo, 0.02 to 0.2 wt % N; 0.02 to 0.2 wt % Nb; and 0.5 to 5.6 wt % slag
forming agent. The components composing the flux cored wire satisfy the
following equations of:
1.5.ltoreq.{(Cr+Mo+1.5Si+0.5Nb)/(Ni+0.5Mn+30C+30N)}.ltoreq.2.3 and
25.ltoreq.PREN (Cr+3.3Mo+16N).ltoreq.45. The welding wire of the invention
forms the suitable weld metal in welding the dual phase structure
stainless steel instead of the single phase steel so that remarkable
effects can be expected in welding equipments of the sea water resistant
austenitic-ferritic stainless steel which are used for various apparatuses
for the chemical industry.
Jaillissez le fil creusé pour l'acier inoxydable duel ayant le flux versé dans une gaine d'acier inoxydable de l'invention, le flux contient, en ce qui concerne tout le poids du fil : % de 0.02 à 0.10 poids C ; % de silicium de 0.10 à 1.0 poids ; % de manganèse de 1.0 à 3.0 poids, % de Cr de 15 à 35 poids, % de Ni de 7.0 à 12.0 poids ; % de MOIS de 1.5 à 3.5 poids, % de 0.02 à 0.2 poids N ; % de 0.02 à 0.2 poids NOTA: ; et % de scories de 0.5 à 5.6 poids formant l'agent. Les composants composant le fil creusé par flux satisfont les équations suivantes de : 1.5.ltoreq.{(Cr+Mo+1.5Si+0.5Nb)/(Ni+0.5Mn+30C+30N)}.ltoreq.2.3 et 25.ltoreq.PREN (Cr+3.3Mo+16N).ltoreq.45. le fil de soudure de l'invention forme le métal approprié de soudure en soudant l'acier inoxydable de structure duelle de phase au lieu de l'acier monophasé de sorte que des effets remarquables puissent être prévus dans des appareils à souder de l'acier inoxydable austénitique-de ferrite résistant d'eau de mer qui sont utilisés pour différents appareils pour l'industrie chimique.