A hyperbranched polyetherketone and a heat-resistant blend of polyvinylchloride with the same. The polyethereketone is synthesized by self-polycondensation of 3,5-bis[4-[(2,3,4,5,6-pentafluorophenyl)carbonyl]phenoxy]-4-hydroxbenzophe none or 3,5-difluoro-4-hydroxybenzophenone, and then substituting 50 to 80 mole % of fluorine atoms present in the side chains and ends of the PEK molecule by polar groups. In addition, a blend of polyvinylchloride can be manufactured using the hyperbranched polyetherketone by a melt blending technique applicable for industrial purpose at a temperature of 180 to 120.degree. C., and thus the blend of polyvinylchloride with the polyetherekentone can be applied to high temperature end-use products such as hot water pipes.

A hyperbranched polyetherketone und eine hitzebeständige Mischung des Polyvinylchlorids mit demselben. Das polyethereketone wird durch Selbst-Self-polycondensation von 3,5-bis[4-[(2,3,4,5,6-pentafluorophenyl)carbonyl]phenoxy]-4-hydroxbenzophe keine oder 3,5-difluoro-4-hydroxybenzophenone und 50 bis 80 Mole % der Fluoratome dann ersetzen synthetisiert, die in den Seitenketten und in den Enden des PEK Moleküls durch polare Gruppen vorhanden sind. Zusätzlich kann eine Mischung des Polyvinylchlorids das hergestellte Verwenden sein hyperbranched polyetherketone durch eine Schmelzmischende Technik, die für industriellen Zweck bei einer Temperatur von 180 auf 120.degree anwendbar ist. C. und folglich die Mischung des Polyvinylchlorids mit dem polyetherekentone können an den Hochtemperaturendverbrauchprodukten wie Heißwasserrohren angewendet werden.

 
Web www.patentalert.com

< (none)

< Process for making multiphase polymeric film having a lamellar structure with controlled permeability and/or controlled mechanical properties

> Golf ball with high coefficient of restitution

> (none)

~ 00091