A maraging steel strip or part and process for manufacture of a strip or of
a part cut out of a strip of cold-rolled maraging steel and hardened by a
hardening heat treatment. In the process, before the hardening heat
treatment is performed, the strip or the part is subjected to cold plastic
deformation with a degree of working greater than 30% and the strip or the
part is subjected to recrystallization annealing in order to obtain a
fine-grained structure with ASTM index higher than 8. The composition by
weight of the maraging steel is: 12%.ltoreq.Ni.ltoreq.24.5%;
2.5%.ltoreq.Mo.ltoreq.12%; 4.17%.ltoreq.Co.ltoreq.20%, Al %.ltoreq.0.15%;
Ti.ltoreq.0.1%; N.ltoreq.0.003%; Si.ltoreq.0.1%; Mn.ltoreq.0.1%;
C.ltoreq.0.005%; S.ltoreq.0.001%; P.ltoreq.0.005%; H.ltoreq.0.0003%;
O.ltoreq.0.001%; iron and impurities resulting from smelting, the chemical
composition also satisfying the relationships:
20%.ltoreq.Ni+Mo.ltoreq.27%; 50.ltoreq.Co.times.Mo.ltoreq.200;
Ti.times.N.ltoreq.2.times.10.sup.-4.
Maraging стальные прокладка или часть и процесс для изготовления прокладки или части cut out прокладки холоднопрокатный maraging стальной и затвердетый твердея обработкой жары. В процессе, прежде чем твердея обработка жары выполнены, прокладка или часть подвергается к холодной пластичной деформации с степенью работы greater than 30% и прокладка или часть подвергаются к отжигу рекристаллизации для того чтобы получить тонкозернистую структуру с индексом более высоко чем 8 ASTM. Состав by weight of maraging сталь является следующим: 12%.ltoreq.Ni.ltoreq.24.5%; 2.5%.ltoreq.Mo.ltoreq.12%; 4.17%.ltoreq.Co.ltoreq.20%, al %.ltoreq.0.15%; Ti.ltoreq.0.1%; N.ltoreq.0.003%; Si.ltoreq.0.1%; Mn.ltoreq.0.1%; C.ltoreq.0.005%; S.ltoreq.0.001%; P.ltoreq.0.005%; H.ltoreq.0.0003%; O.ltoreq.0.001%; утюг и примеси приводящ к от выплавки, химическийа состав также удовлетворяя отношения: 20%.ltoreq.Ni+Mo.ltoreq.27%; 50.ltoreq.Co.times.Mo.ltoreq.200; Ti.times.N.ltoreq.2.times.10.sup.-4.