A plating-free solid wire for arc welding has pits opening on its
circumference, and wider inside than at each opening, and/or pits having a
portion non-irradiated with an externally incoming light. A sulfide and a
polyisobutene-containing oil are present in the pits and/or on the wire
surface, the latter being present in an amount of 0.1-2 g/10 kg of wire.
Twenty or more pits are present in total per and along wire circumference.
The effective pit length ratio is 0.5% inclusive-50% exclusive. 0.1-2 g of
the oil is present per 10 kg of wire. 0.01-0.5 g/10 kg of
0.1-10-.mu.m-particle-dia MoS.sub.2 is present in "bottleneck-like and/or
cave-like pits", on the wire surface or immediately under the wire
surface. A 2-10 mass ppm/total wire mass of K compound in K is present in
the pits and/or on the wire surface. These ensure good feedability and
lubricating properties, and less spatters.
Ένα επένδυση-ελεύθερο στερεό καλώδιο για τη συγκόλληση τόξων έχει τα κοιλώματα ανοίγοντας στην περιφέρειά του, και το ευρύτερο εσωτερικό απ'ό,τι σε κάθε άνοιγμα, ή/και τα κοιλώματα που έχουν μια μερίδα μη εκτεθειμένη σε ακτινοβολία με ένα εξωτερικά εισερχόμενο φως. Ένα σουλφίδιο και ένα πολυησοψuτενε-περιέχοντας πετρέλαιο είναι παρόντα στα κοιλώματα ή/και στην επιφάνεια καλωδίων, τα τελευταία που είναι παρόντα σε ένα ποσό 0,1-2 g/10 κλ του καλωδίου. Είκοσι ή περισσότερα κοιλώματα είναι παρόντα στο σύνολο ανά και κατά μήκος περιφέρεια καλωδίων. Η αποτελεσματική αναλογία μήκους κοιλωμάτων είναι 0,5% inclusive50% αποκλειστικό. 0,1-2 γ του πετρελαίου είναι παρόν ανά 10 κλ του καλωδίου. 0.01-0.5 g/10 κλ του 0,1-10-.μu.μ-μόριο- dia MoS.sub.2 είναι παρόν στα "δυσχέρεια-όπως ή/και σπηλιά-όπως κοιλώματα", στην επιφάνεια καλωδίων ή αμέσως κάτω από την επιφάνεια καλωδίων. Μια 2-10 μάζα PPM/i συνολική μάζα καλωδίων της ένωσης Κ στο Κ είναι παρούσες στα κοιλώματα ή/και στην επιφάνεια καλωδίων. Αυτοί εξασφαλίζουν το καλό feedability και τις λαδώνοντας ιδιότητες, και λιγότερα spatters.