Process for producing regular porous pearl cellulose with a particle size in the range from 2 to 1,000 .mu.m, comprising the steps: a) a cellulose having a degree of polymerisation in the range from 150 to 2,000 is dissolved in a solvent to form a solution of 0.5 to 25% by mass, b) the cellulose solution is finely divided and dispersed in a dispersant which is immiscible with said solution and has a viscosity in the range from 10 to 80,000 mPa.multidot.s, c) the dispersed solution particles are solidified to regular pearl particles by precipitating with a liquid precipitating agent miscible with the solvent (1) after cooling the dispersion to below the melting temperature of the cellulose solution and separating the frozen particles of the cellulose solution from the dispersant or (2) directly in the dispersion, and d) the pearl particles are separated from the liquid mixture of solvent, precipitating agent and possibly dispersant.

Proceso para producir la celulosa porosa regular de la perla con un tamaño de partícula en la gama a partir del 2 al mu.m 1.000, abarcando los pasos: a) una celulosa que tiene un grado de polimerización en la gama a partir del 150 a 2.000 es disuelta en un solvente para formar una solución de 0.5 a el 25% por la masa, b) la solución de la celulosa se divide finalmente y dispersado en un dispersor que sea inmiscible con la solución dicha y tenga una viscosidad en la gama a partir del 10 a 80.000 mPa.multidot.s, c) las partículas dispersadas de la solución se solidifican a las partículas regulares de la perla precipitándose con un agente de precipitación líquido miscible con el (1) solvente después de refrescar la dispersión debajo de la temperatura que derrite de la solución de la celulosa y de separar las partículas congeladas de la solución de la celulosa del dispersor o (2) directamente en la dispersión, y d) las partículas de la perla se separan de la mezcla líquida del solvente, precipitando el agente y posiblemente el dispersor.