A Zn--Co--W alloy electroplated steel sheet with excellent corrosion resistance and weldability, and an electrolyte for manufacturing same are provided. The plating layer consisting of Co: 0.1-3.0 wt %, and zinc: balance, is formed on the steel sheet and all tungsten plating is carried out with metallic tungsten; an electrolyte for manufacturing a Zn--Co--W alloy electroplated steel sheet, comprising zinc chloride: 60-200 g/l, cobalt chloride: 0.1-6.0 g/l, tungsten: 0.1-4.0 g/l, citric acid: 0.5-10.0 g/l, polyethylene glycol: 0.1-2.0 m/l and electric conductive aid: 30-400 g/l, wherein substantially all of the tungsten ions form a complex compound with citric acid, thereby preventing formation of sludge; and a Zn--Co--W alloy electroplated steel sheet, on which a plating layer is formed by electroplating the steel in the electrolyte.

Zn -- Co -- de legering van W galvaniseerde staalplaat met uitstekende corrosieweerstand en lasbaarheid, en een elektrolyt voor productiezelfde wordt verstrekt. De platerenlaag die uit Co bestaat: 0.1-3.0 gewicht %, en zink: het saldo, wordt gevormd op de staalplaat en al wolframplateren wordt uitgevoerd met metaalwolfram; een elektrolyt voor de productie van Zn -- Co -- de legering van W galvaniseerde staalplaat, bestaand zink uit chloride: 60-200 g/l, kobaltchloride: 0.1-6.0 g/l, wolfram: 0.1-4.0 g/l, citroenzuur: 0.5-10.0 g/l, polyethyleenglycol: 0.1-2.0 m/l en elektrische geleidende hulp: 30-400 g/l, waarin de elk van wolframionen wezenlijk een complexe samenstelling met citroenzuur vormen, daardoor verhinderend vorming van modder; en Zn -- Co -- de legering van W galvaniseerde staalplaat, waarop een platerenlaag door het staal in de elektrolyt te galvaniseren wordt gevormd.