A weldable structural steel product having fine complex precipitates of TiN and CuS is provided which contains, in terms of percent by weight, 0.03 to 0.17%C, 0.01 to 0.05% Si, 0.4 to 2.0% Mn, 0.005 to 0.2% Ti, 0.0005 to 0.1% Al, 0.008 to 0.030% N, 0.0003 to 0.01% B, 0.001 to 0.2% W, 0.1 to 1.5% Cu, at most 0.03% P, 0.003 to 0.05% S, at most 0.005% O, and balance Fe and incidental impurities while satisfying conditions of 1.2.ltoreq.Ti/N.ltoreq.2.5, 10.ltoreq.N/B.ltoreq.40, 2.5.ltoreq.Al/N.ltoreq.7, 6.5.ltoreq.(Ti+2Al+4B)/N.ltoreq.14, and 10.ltoreq.Cu/S.ltoreq.90, and having a microstructure essentially consisting of a complex structure of ferrite and pearlite having a grain size of 20 .mu.m or less.

Un prodotto saldabile dell'acciaio per costruzioni edili che ha benissimo precipitati complessi di latta e CuS è fornito che contiene, nei termini dei percento da peso, 0.03 a 0.17%C, 0.01 - 0.05% siliconi, 0.4 - 2.0% il manganese, 0.005 - 0.2% Ti, 0.0005 - 0.1% Al, 0.008 - 0.030% N, 0.0003 - 0.01% B, W, 0.1 - 1.5% S del Cu 0.001 - 0.2%, tutt'al più 0.03% P, 0.003 - 0.05%, tutt'al più 0.005% O e Fe dell'equilibrio ed impurità fortuite mentre stati di soddisfazione di 1.2.ltoreq.Ti/N.ltoreq.2.5, di 10.ltoreq.N/B.ltoreq.40, di 2.5.ltoreq.Al/N.ltoreq.7, di 6.5.ltoreq.(Ti+2Al+4B)/N.ltoreq.14 e di 10.ltoreq.Cu/S.ltoreq.90 e dell'avere una microstruttura essenzialmente essere fatta di una struttura complessa di ferrite e di pearlite che hanno un formato di grano di mu.m 20 o di di meno.