A method for producing an orthopaedic implant having enhanced fatigue
strength. A forged implant substrate having an elongated stem is
incorporated with a melting point lowering substance. Then, metal
particles are sintered to the substrate, forming a porous layer on the
substrate which enhances bone in growth or the mechanical interlock with
bone cement. Advantageously, the sintering occurs at a lower temperature
than if the substance were not incorporated into the substrate, which in
turn results in an enhanced fatigue strength of the inventive implant. The
fatigue strength of a forged or cast implant can also be improved by
nitrogen diffusion hardening and/or thermally processing the implant after
the porous coating is adhered by sintering. Further, the fatigue strength
can be further improved by combining incorporating the melting point
lowering substance with nitrogen diffusion hardening and/or aging
treatment subsequent to sintering.
Метод для производить протезное имплантирует увеличивать прочность усталости. Выкованное имплантирует субстрат имея elongated стержень включено при точка плавления понижая вещество. После этого, частицы металла спечены к субстрату, формируя пористый слой на субстрате который увеличивает косточку в росте или механически блокировку с цементом косточки. Выгодн, спекать происходит на более низкой температуре чем если вещество не было включено в субстрат, то который в свою очередь приводит к в увеличенной прочности усталости изобретательного имплантирует. Прочность усталости ковать или бросание имплантируют могут также быть улучшены диффузией азота твердея and/or термально обрабатывать имплантирует после того как пористое покрытие придержано путем спекать. Более потом, прочность усталости может более в дальнейшем быть улучшена путем совмещать включающ точку плавления понижая вещество с обработкой диффузии азота твердея and/or старея затем к спекать.