A method of producing hexagonal (system) ferrite, wherein the hexagonal
(system) ferrite having an average tabular diameter of 10 to 40 nm and a
coercive force (Hc) of 135 to 400 kA/m is treated with an organic compound
containing a polar group having an acid dissociation constant (pKa) of 4
or below and/or a salt thereof when the ferrite is recovered and washed,
and a magnetic recording medium comprising a support having thereon a
non-magnetic layer comprising a non-magnetic powder and on the
non-magnetic layer a magnetic layer comprising a ferromagnetic powder,
wherein the ferromagnetic powder comprises a hexagonal (system) ferrite
magnetic powder having an average tabular diameter of 10 to 40 nm and a
coercive force (Hc) of 135 to 400 kA/m and being subjected to treatment
with an organic compound containing a polar group having an acid
dissociation constant (pKa) of 4 or below and/or a salt thereof.
Un metodo di produrre la ferrite esagonale (del sistema), in cui la ferrite esagonale (del sistema) che ha un diametro tabulare medio di 10 a 40 il nm e una forza coercive (Hc) di 135 - 400 kA/m è trattata con un residuo organico che contiene un gruppo polare che ha un costante acido di dissociazione (pKa) di 4 o sotto e/o di un sale di ciò quando la ferrite è recuperata e lavata e un mezzo magnetico della registrazione che contiene un supporto che ha su ciò uno strato non magnetico contenere una polvere non magnetica e sullo strato non magnetico un lo strato magnetico che contiene una polvere ferromagnetica, in cui la polvere ferromagnetica contiene una polvere magnetica della ferrite esagonale (del sistema) che ha medio un tabulare un diametro di 10 a 40 nm e una forza coercive (Hc) di 135 - 400 kA/m ed essendo sottoponendo al trattamento con un residuo organico che contiene un gruppo polare che ha un costante acido di dissociazione (pKa) di 4 o sotto e/o di un sale di ciò.