The present invention relates to a Ni-base brazing alloy. The alloy has a
good wettability toward a material to be brazed when melting, an excellent
corrosion resistance and a high strength. The alloy is used for process of
joining two pieces of metal such as stainless steel. The alloy contains Cr
in an mount of 25 to 35% by weight, P in an amount of 4 to 8% by weight,
Si in an amount of 3 to 6% by weight, wherein the total amount of P and Si
is 9 to 11.5% by weight, at least one selected from a group consisting of
Al, Ca, Y and misch metal in an amount of 0.01 to 0.10% by weight, and the
balance of Ni and unavoidable impurities.
La actual invención se relaciona con una aleación que suelda de la Ni-base. La aleación tiene un buen wettability hacia un material que se soldará al derretir, una resistencia a la corrosión excelente y una alta fuerza. La aleación se utiliza para el proceso de ensamblar dos pedazos de metal tales como acero inoxidable. La aleación contiene el cr en un montaje de 25 a el 35% al lado del peso, P en una cantidad de 4 a el 8% al lado del peso, silicio en una cantidad de 3 a el 6% al lado del peso, en donde la cantidad total de P y silicio es 9 a 11.5% al lado de peso, por lo menos uno seleccionado de un metal del al, del CA, de Y y del misch del grupo que consiste en en una cantidad de 0.01 a 0.10% por el peso, y del equilibrio del Ni y de las impurezas inevitables.