A process for the production of an ionic transition metal catalyst in
supported form than is highly productive under gas phase olefin
polymerization conditions. In the process a an aluminum alkyl is added to
a suitable solvent after which a neutral metallocene compound is added to
the solution under stirring in a quantity that provides for a ratio of Al
to transition metal of at least 25:1. To this metallocene-aluminum alkyl
solution is next added an ionic compound the anionic portion of which is a
non-coordinating anion under stirring until all materials are dissolve.
The ionic compound is added in a quantity that provides for a ratio of NCA
to transition metal of at least 1:1. Next the support particles are added
to the solution and thereafter the solution is heated to at least
40.degree. C. and held at this elevated temperature for at least 0.5 hour.
Thereafter the solvent is removed and the supported catalyst is dried
under vacuum.
Un procédé pour la production d'un catalyseur ionique en métal de transition sous la forme soutenue qu'est les états de dessous fortement productifs de polymérisation d'oléfine de phase gaseuse. Dans le processus un alkyl en aluminium est ajouté à un dissolvant approprié après quoi un composé neutre de metallocene est ajouté à la solution sous l'agitation dans une quantité qui prévoit un rapport d'Al au métal de transition au moins de 25:1. À cet metallocene-aluminium la solution alkylique est après ajoutée un composé ionique dont la partie anionique est un anion non-coordonné sous l'agitation jusqu'à ce que tous les matériaux soient se dissolvent. Le composé ionique est ajouté dans une quantité qui prévoit un rapport de NCA au métal de transition au moins de 1:1. Après les particules de soutien sont ajoutées à la solution et ensuite la solution est chauffée au moins à 40.degree. C. et tenu à cette température élevée pour au moins 0.5 heure. Ensuite le dissolvant est enlevé et le catalyseur soutenu est séché sous vide.