The present invention provides block copolymers which have reduced solvent
sensitivity and which overcome the foregoing disadvantages. In one
embodiment of the present invention, there is provided an asymmetric block
copolymer of the structure A-B-C-A wherein each A block is formed of a
vinyl aromatic hydrocarbon, preferably styrene, and has a weight average
molecular weight of 5,000 to 50,000. B is a polybutadiene block having a
weight average molecular weight of 1,000 to 15,000 and a vinyl content of
less than 25% by weight, and C is an elastomeric conjugated diene polymer
block having a weight average molecular weight of 25,000 to 200,000 and
has a vinyl content of 30 to 90%, preferably 35 to 80%, and most
preferably 35 to 70% by weight. In the second embodiment of the present
invention, there is provided a hydrogenated block copolymer of the formula
A-B-C-B-A wherein A, B, and C have the definitions set forth above.
Η παρούσα εφεύρεση παρέχει copolymers φραγμών που έχουν μειώσει τη διαλυτική ευαισθησία και που υπερνικούν τα προηγούμενα μειονεκτήματα. Σε μια ενσωμάτωση της παρούσας εφεύρεσης, παρέχεται ασυμμετρικό copolymer φραγμών της δομής α-β-γ-α όπου κάθε ο φραγμός Α διαμορφώνεται ενός βινυλίου αρωματικού υδρογονάνθρακα, κατά προτίμηση στυρόλιο, και έχει ένα μέσο μοριακό βάρος βάρους 5.000 έως 50,000. το β είναι ένας polybutadiene φραγμός που έχει ένα μέσο μοριακό βάρος βάρους 1.000 έως 15.000 και ένα βινυλίου περιεχόμενο λιγότερο από 25% από το βάρος, και γ είναι ένας elastomeric κλιμένος πολυμερής φραγμός διένιων που έχει ένα μέσο μοριακό βάρος βάρους 25.000 έως 200.000 και έχει ένα βινυλίου περιεχόμενο 30 ως 90%, κατά προτίμηση 35 80%, και κατά προτίμηση 35 70% από το βάρος. Στη δεύτερη ενσωμάτωση της παρούσας εφεύρεσης, παρέχεται υδρογονωμένο copolymer φραγμών του τύπου α-β-γ-β-α όπου το Α, το β, και το γ εκθέτουν τους ορισμούς ανωτέρω.