A dispersion control fiber and a method of manufacturing a large size
preform are provided. In one embodiment, the dispersion control fiber
comprises a core composed of SiO.sub.2, GeO.sub.2, P.sub.2 O.sub.5 and
Freon, and a cladding composed of SiO.sub.2, GeO.sub.2, P.sub.2 O.sub.5,
and Freon. The P.sub.2 O.sub.5 content is selected not to exceed 10% of
the total weight of a compound composing the core. An embodiment of the
method of manufacturing a large size preform for a dispersion control
fiber by an MCVD process comprises depositing SiO.sub.2, GeO.sub.2,
P.sub.2 O.sub.5, and Freon in an inner periphery of a deposition tube to
form a cladding layer, and depositing SiO.sub.2, GeO.sub.2, P.sub.2
O.sub.5 and Freon on an inner periphery of the cladding layer to form a
core layer.
Uma fibra do controle da dispersão e um método de manufaturar uma pré-forma grande do tamanho são fornecidos. Em uma incorporação, a fibra do controle da dispersão compreende um núcleo composto de SiO.sub.2, de GeO.sub.2, de P.sub.2 O.sub.5 e Freon, e de um cladding composto de SiO.sub.2, de GeO.sub.2, de P.sub.2 O.sub.5, e de Freon. O índice de P.sub.2 O.sub.5 é selecionado para não exceder 10% do peso total de um composto que compõe o núcleo. Uma incorporação do método de manufaturar uma pré-forma grande do tamanho para uma fibra do controle da dispersão por um processo de MCVD compreende SiO.sub.2, GeO.sub.2, P.sub.2 O.sub.5, e Freon depositando em uma periferia interna de um tubo do deposition para dar forma a uma camada do cladding, e SiO.sub.2, GeO.sub.2, P.sub.2 O.sub.5 e Freon depositando em uma periferia interna da camada do cladding para dar forma a uma camada do núcleo.