Disclosed is a method for the preparation of polymeric phosphate flame
retardants with a molecular weight of at least about 1500 and a softening
temperature of at least about 10.degree. C. comprising the steps of (a)
reacting a phosphorus oxyhalide with a monohydroxyaromatic compound, (b)
removing substantially all of any remaining phosphorus oxyhalide; (c)
reacting the monoaryldichlorophosphate product with a dihydroxyaromatic
compound and (d) reacting the product of step (c) with a
monohydroxyaromatic compound. The solid polymeric flame retardant has a
linear structure and less than 10 ppm halogen bound to phosphorus. Also
disclosed are resinous compositions comprising the solid polymeric
phosphate made by the method of the invention and at least one other
polymeric resin.
Onthuld wordt een methode voor de voorbereiding van de polymere vertragers van de fosfaatvlam met een moleculegewicht minstens ongeveer 1500 en een zacht wordende temperatuur van op zijn minst over 10.degree. C. bestaand uit de stappen van (a) reagerend fosforoxyhalide met een monohydroxyaromatic samenstelling, (b) wezenlijk verwijderend elk van om het even welke resterende fosforoxyhalide; (c) reagerend het monoaryldichlorophosphateproduct met een dihydroxyaromatic samenstelling en (d) reagerend het product van stap (c) met een monohydroxyaromatic samenstelling. De stevige polymere vlamvertrager heeft een lineaire structuur en minder dan 10 p.p.m.halogeen verbindend aan fosfor. Ook onthuld worden de harsachtige samenstellingen bestaand uit het stevige polymere fosfaat dat door de methode van de uitvinding en minstens één andere polymere hars wordt gemaakt.