There are provided a rolling bearing comprising an outer race, an inner
race, and a plurality of rolling elements each interposed between the
outer race and the inner race, at least one of the outer race, the inner
race and the rolling elements being made of a steel consisting
essentially, by mass, of 0.40 to 0.60% C, not more than 0.5% Si, not more
than 0.5% Mn, not less than 8.0% but less than 10.0% Cr, and the balance
Fe and incidental impurities, said steel having a hardness not less than
740 HV, carbides contained in said steel having a long size not more than
1.2 .mu.m, and an amount of said carbides being not more than 3.5% in area
%, and a method of producing the rolling bearing.
Werden einem Rollenlager zur Verfügung gestellt, das ein äußeres Rennen, einen Innenring und eine Mehrzahl von den Rollenelementen jede enthält, die zwischen dem äußeren Rennen und dem Innenring, an wenigem des äußeren Rennens, des Innenrings und der Rollenelemente gebildet werden von einem Stahl vermittelt wird, der im Wesentlichen, durch Masse, von 0.40 bis 0.60% C, nicht mehr als 0.5% Silikon, nicht mehr als 0.5% Mangan, nicht weniger als 8.0% aber weniger Cr als 10.0% und die Balance F.E.- und beiläufigen Verunreinigungen, der besagte Stahl besteht, der eine Härte nicht weniger als 740 Hochspg, die Karbide hat, die im besagten Stahl enthalten werden, der ein langes Größe nicht mehr mu.m als 1.2 hat, und eine Menge besagte Karbide, die nicht mehr als 3.5% im Bereich % sind, und eine Methode des Produzierens des Rollenlagers.