Autodeposition compositions for polymeric coatings of reduced gloss are
prepared using resins having at least one hydroxy group and at least one
epoxy group per molecule, a low temperature crosslinker and a high
temperature crosslinker. The low temperature crosslinker forms a reactive
prepolymer that may be subsequently mixed or emulsified with a high
temperature crosslinker to form an autodeposition composition.
Alternatively, a hybrid crosslinking agent may be utilized which contains
both free isocyanate groups reactive at a relatively low temperature with
the resin and at least one functional group capable of reacting with the
resin only at a relatively elevated temperature. When deposited and cured,
the resulting coating has a matte finish that is resistant to surface
defects.
Las composiciones de Autodeposition para las capas poliméricas de lustre reducido están preparadas usando las resinas que tienen por lo menos un grupo hydroxy y por lo menos un grupo de epoxy por la molécula, un crosslinker de la baja temperatura y un crosslinker de alta temperatura. El crosslinker de la baja temperatura forma un prepolymer reactivo que se pueda mezclar o emulsionar posteriormente con un crosslinker de alta temperatura para formar una composición del autodeposition. Alternativomente, un agente de reticulación híbrido puede ser utilizado que contiene ambos grupos libres del isocianato reactivos en una temperatura relativamente baja con la resina y por lo menos un grupo funcional capaces de reaccionar con la resina solamente en una temperatura relativamente elevada. Cuando está depositada y curada, la capa que resulta tiene un final mate que sea resistente a los defectos superficiales.