This invention relates to a polyisocyanate composition having a mean
functionality of greater than 3, obtained by polycondensation of
diisocyanate or triisocyanate monomers.
The invention also relates to a reactive coating composition comprising the
isocyanate composition defined above and a polyol having a hydroxyl number
of between approximately 50 and approximately 250 and a number [lacuna]
molar mass of between approximately 500 and approximately 15 000, said
coating composition exhibiting a good pot life and a rapid rate of
crosslinking at ambient temperature, to produce a crosslinked coating
possessing good properties of surface hardness, of flexibility and of
impact resistance.
Questa invenzione riguarda una composizione nel polyisocyanate che fa ottenere una funzionalità media più notevolmente di di 3, tramite la policondensazione dei monomeri del triisocyanate o del diisocyanate. L'invenzione inoltre si riferisce ad una composizione ricoprente reattiva che contengono la composizione nell'isocianato definita sopra e un polyol che ha un numero dell'idrossile tra compreso di circa 50 e circa 250 e una massa molare di numero [ lacuna ] tra compreso di circa 500 e circa 15 000, composizione ricoprente detta esibenti una buona durata di POT e un tasso veloce di unire con legami atomici incrociati alla temperatura ambientale, per produrre un rivestimento unito con legami atomici incrociati che possiede le buone proprietà di durezza di superficie, di flessibilità e di resistenza all'urto.