A negative active material for a lithium secondary battery includes a
graphite-like carbon material having an intensity ratio I(110)/I(002) of
an X-ray diffraction peak intensity I(002) at a (002) plane to an X-ray
diffraction peak intensity I(110) at a (110) plane of less than 0.2. The
negative active material prepared by dissolving a coar tar pitch or a
petroleum pitch in an organic solvent to remove insoluble components
therefrom, heat-treating the pitch at a temperature in the range of 400 to
450.degree. C. for 4 hours or more under an inert atmosphere to thereby
produce at least 50 weight percent of mesophase particles based on the
pitch, coking the pitch including mesophase particles, carbonizing the
coked pitch, pulverizing the carbonized pitch; and graphitizing the
pulverized pitch.
Een negatief actief materiaal voor een lithium secundaire batterij omvat een grafiet-als koolstofmateriaal dat een intensiteitsverhouding I (110)/I (002) van een X-ray diffractie piekintensiteit I heeft (002) bij een (002) vliegtuig aan een X-ray diffractie piekintensiteit I (110) bij een (110) vliegtuig van minder dan 0,2. Het negatieve actieve materiaal die door een coar teerhoogte op te lossen wordt voorbereid of een aardolie werpt in een organisch oplosmiddel om onoplosbare componenten te verwijderen daarvan, hitte-behandelend de hoogte bij een temperatuur in de waaier van 400 aan 450.degree. C. 4 uren of meer onder een inerte atmosfeer daardoor minstens 50 gewichtenpercenten mesofasedeeltjes veroorzaken die op de hoogte worden gebaseerd, die de hoogte met inbegrip van mesofasedeeltjes vercookst, die de gevercookste hoogte carboniseren, die de gecarboniseerde hoogte verpulvert; en graphitizing de verpulverde hoogte.