A steel sheet with a thickness of at least 0.30 mm is made of an ultra-low
carbon steel with a chemical composition including C: at most 0.010 %, Si:
at most 0.5 %, Mn: at most 1.5 %, P: at most 0.12 %, S: at most 0.030 %,
Ti: at most 0.10 %, Al: at most 0.08 %, and N: at most 0.0080 %. The total
number of non-metallic inclusions observed under a microscope in sixty
fields in a sample prepared in accordance with JIS G0555 is at most 20.
During manufacture of the steel, the amount of FeO+MnO in slag in a ladle
at the time of continuous casting is controlled to at most 15 %, and the
throughput at the time of casting is made at most 5 tons per minute. The
steel sheet does not develop pin hole defects or press cracks caused by
inclusions when used for applications such as motor housings or oil filter
housings requiring severe press forming.
Uma folha de aço com uma espessura ao menos de 0.30 milímetro é feita de um aço de carbono ultra-baixo com uma composição química including C: em a maioria 0.010 %, silicone: em a maioria 0.5 %, manganês: em a maioria 1.5 %, P: em a maioria 0.12 %, S: em a maioria 0.030 %, ti: em a maioria 0.10 %, al: em a maioria 0.08 %, e em N: em a maioria 0.0080 %. que o número total dos inclusions não metálicos observados sob um microscópio em sessenta campos em uma amostra se preparou de acordo com JIS G0555 é em a maioria 20. Durante a manufatura do aço, a quantidade de FeO+MnO no slag em um ladle na altura da carcaça contínua é controlada a a maioria 15 %, e o throughput na altura da carcaça é feito em a maioria 5 de toneladas por o minuto. A folha de aço não desenvolve o pino defeitos do furo nem não pressiona as rachaduras causadas por inclusions quando usada para aplicações tais como as carcaças de carcaças de motor ou de filtro do óleo que requerem dar forma severo da imprensa.