The invention provides a method for producing barium titanate-based
particulate compositions. The method includes a heat treatment step,
separate from a sintering step, that involves treating a barium
titanate-based particulate composition at a temperature between about
700.degree. C. and about 1150.degree. C. to increase average particle
size. The increased average particle size can improve the electrical
properties (i.e., dielectric constant and dissipation factor) of the
heat-treated composition as compared to the composition prior to heat
treating. The heat-treated composition may be further processed, for
example, by producing a dispersion which may be cast and sintered to form
a dielectric layer in electronic components including MLCCs.
La invención proporciona un método para producir las composiciones de partículas titanate-basadas bario. El método incluye un paso del tratamiento de calor, a parte de un paso de la sinterización, que implica el tratar de una composición de partículas titanate-basada bario en una temperatura entre alrededor 700.degree. C. y sobre 1150.degree. C. para aumentar el tamaño de partícula medio. El tamaño de partícula medio creciente puede mejorar las características eléctricas (es decir, factor de la constante dieléctrica y de la disipación) de la composición sometida a un tratamiento térmico con respecto a la composición antes de tratar del calor. La composición sometida a un tratamiento térmico se puede procesar más a fondo, por ejemplo, produciendo una dispersión que se pueda echar y sinterizar para formar una capa dieléctrica en componentes electrónicos incluyendo MLCCs.