An object of the present invention is to provide a hydrogen absorbing alloy
which can improve a high rate discharge property while suppressing
particle size reduction, exhibits cycle life characteristics equal to or
higher than those of conventional alloys even when its cobalt content is
decreased, and has a high capacity. Specifically, the present invention
provides a hydrogen absorbing alloy having a CaCu.sub.5 type crystal
structure in its principal phase, wherein the La content in the alloy is
in the range of 24 to 33% by weight and the Mg or Ca content in the alloy
is in the range of 0.1 to 1.0% by weight, as well as the aforesaid alloy
wherein the Co content in the alloy is not greater than 9% by weight.
Un oggetto di presente invenzione è fornire una lega assorbente dell'idrogeno a cui può migliorare una proprietà di scarico di alto tasso mentre sopprimono la riduzione di dimensione delle particelle, esibisce le caratteristiche di vita del ciclo uguali o più superiore a quelle delle leghe convenzionali anche quando il relativo soddisfare del cobalto è diminuito ed ha una capacità elevata. Specificamente, la presente invenzione fornisce una lega assorbente dell'idrogeno che ha CaCu.sub.5 un tipo struttura di cristallo nella relativa fase principale, in cui il soddisfare della La nella lega è nella gamma di 24 - 33% di peso ed il soddisfare di CA o del magnesio nella lega è nella gamma di 0.1 - 1.0% di peso, così come la lega suddetta in cui il soddisfare di Co nella lega non è più grande di 9% di peso.