A polypropylene-based calendered or injection-molded article satisfying the
requirements of (1) having a tensile modulus TM of 5 MPa or higher and (2)
having, when measured by a differential scanning calorimeter (DSC), no
melting point or a melting point Tm (.degree. C.) satisfying the formula:
TM.gtoreq.5.times.Tm-450, is less tacky and excellent in flexibility and
transparency. Such a polypropylene-based calendered or injection-molded
article is produced from a propylene polymer satisfying the requirements
of (1) having a component soluble in a 25.degree. C. hexane in a content
H25 of 0 to 80% by weight; (2) having, when measured by a differential
scanning calorimeter (DSC), no melting point or a melting point Tm
(.degree. C.) satisfying the formula: .DELTA.H.gtoreq.6.times.(Tm-140)
wherein .DELTA.H is a melting endotherm (J/g); and (3) having an intrinsic
viscosity [.eta.] of 1 to 3 dl/g as measured at 135.degree. C. in
tetralin.
Polypropylène-basé calandré ou article injection-moulé répondant aux exigences (1) d'avoir un module de tension TM de 5 MPa ou plus haut et (2) ayant, une fois mesuré par un calorimètre de balayage différentiel (DSC), aucun point de fusion ou un point de fusion Tm (degree. C.) satisfaire la formule : TM.gtoreq.5.times.Tm-450, est moins visqueux et excellent en flexibilité et transparent. L'article calandré ou injection-moulé un tel polypropylène-basé est produit à partir d'un polymère de propylène répondant aux exigences (1) d'avoir un soluble de composant dans un 25.degree. Hexane de C. dans une teneur H25 de 0 à 80% en poids ; (2) ayant, une fois mesuré par un calorimètre de balayage différentiel (DSC), aucun point de fusion ou un point de fusion Tm (degree. C.) satisfaire la formule : DELTA.H.gtoreq.6.times.(Tm-140) Où le DELTA.H est un endotherm de fonte (J/g) ; et (3) ayant une viscosité intrinsèque [ eta. ] de 1 à 3 dl/g la mesure étant faite à 135.degree. C. en tétraline.